EWAC Flux Cored Wire
| Product | Main Uses | Tensile Strength in PSI | Hardness |
|---|---|---|---|
| EWAC O 510 | Good impact resistance with good comprehensive strength. Joining of Crane jibs, Truck chassis & Heavy equipment maintenance | 70,000 | -- |
| EWAC O 521 | For repair & joining application on difficult steels, low & high alloy & Mn steels. Also suitable for using as cushion layer under wear resistant coating | 92,000 | -- |
| EWAC O 52B | Good resistance to compression and plastic deformation. Multi-pass deposit capability. | -- | 25 to 35 HRc (3 layer) |
| EWAC O 540 | For buttering layers prior to harder overlays & wear preventive coating of Crane wheels, Crusher cylinder, Shovel buckets etc. | -- | - As Deposited: 90 HRb(3 layer) - Work Hardened: 42 HRc (3 layer) |
| EWAC OA 564 | Excellent resistance to impact, galling & scoring. For re-conditioning of Drive sprockets, Crusher rolls & Jaws, Track pads, Dozer blades etc. | 78,000 | -- |
| EWAC O 570 | Excellent resistance to Grinding abrasion with compression & impact. For hard-facing of Excavator teeth, Dredger buckets, Crusher augurs, Conveyor parts etc. | -- | 50 – 58 HRc (3 layer) |
| EWAC O 630 | Very high hardness achieved on ferritic steels. Good weldability and high deposition rate. | -- | 62 – 67 HRc (2 layer) |
| EWAC O 606 | Single pass provides optimum, intrinsic properties. Slag free deposit save weld cleaning time. | -- | 60 – 68 HRc |
| EWAC O 512 | Excellent resistance to abrasion & erosion upto 650 Deg. Hard-facing of Sinter handling equipment, Coke pusher shoes, Clinker conveyor chains etc. | -- | 58-64 HRc (3 layer) |
| EWAC O 517 | High resistance to impact, pressure & abrasion. Ideal for thick, multi-pass, protective coatings. | -- | 52 – 58 HRc |
| OA 511 | Abrasion resistance with good compressive strength. Hard-facing of Crusher parts, Conveyor screws, Mantles, Mill guides, Bucket teeth etc. | -- | 50-60 HRc (3 layer) |
| OA 562 | Good resistance to compression & plastic deformation. For re-building & reclamation of Chain guide rolls, Worn parts on bulldozers, severely worn out parts | -- | 25-35 HRc (3 layer) |
| OA 566 | Excellent impact resistance & good compressive strength. Joining of Crane jibs, Truck chassis & Heavy equipment maintenance | 69,000 | -- |
| OA 600 | Rapid deposition rate. No slag. Superior wear resistance. High Hardness. | -- | 56-62 HRc |
| OA 6001 | Formation of stress relieving cracks to minimise distortion. Resistant to flame cutting – use plasma arc process. | -- | 60 – 68 HRc (3 layer) |
| OA 688 | Repair & re-conditioning of Bearing housing, Gears, Jaw crusher plates. Designed for joining MS, Low alloy, Medium alloy, SS & Dissimilar steels | 1,05,000 | -- |
| OA 2110 | Joining of Crane jibs, Truck chassis & Heavy equipment maintenance. Impact resistance with good compressive strength | 71,000 | -- |
| OA 3205 | Excellent resistance to impact & abrasion-Work hardens to service. Ideal application Track pads, Crusher hammers, Blow bar & bucket repairs | -- | - As Deposited: 16 - 22 HRc (3 layer) - Work Hardened: 35 - 45 HRc (3 layer) |
| OA 3302 | Versatile austenitic Cr Ni Mn alloy for high resistance to impact, pressure & metal to metal wear-ideal application -Gyratory crusher cones, Drive sprockets, Mill guides etc. | -- | - As Deposited: 85 – 90 HRb (3 layer) - Work Hardened: 25 – 30 HRb (3 layer) |
| OA 3952 | Refractory carbides in tough matrix withstands abrasion, erosion & corrosion. Ideal application Sinter handling equipment, Coke crusher shoes, Hot slag conveyor. | -- | 58 – 63 HRc (2 layer) |
| OA 4415 | Special heat treatment alloy with excellent resistance to impact & compressive load. Ideal for wear protection on Drill bits, Grab buckets, Dragline teeth, Crusher hammer etc. | -- | 52 – 55 HRc (3 layer) |
| OA 4601 | Excellent resistance to abrasion combined with impact & compression. Ideal application in quarry, cement, dredging & foundry industries | -- | 50 – 55 HRc (3 layer) |
| OA 4625 | Weld metal gives good resistance to abrasion, pressure & moderate impact conditions. Ideal application Screw conveyor, Crusher hammers, Track rollers etc. | -- | 46 – 52 HRc (2 layer) |
| OA 4907 | Continuous electrode for rapid joining, fillet welding & build of low carbon steels. Repair to Machine bases, Housings, Tanks, Maintenance of heavy mining equipment | 80,000 | 20 – 30 HRc |
| DO* 390 N | Revolutionary Nano technology wire for severe abrasion & erosion at elevated temperatures-750 Deg service condition. Ideal application Grizzly bars, Exhaust fans, Mixer blades, Furnace chutes | -- | - 64 – 66 HRc (1st layer) - 66 - 68 HRc (2nd layer) |
| EWAC G-571 D | Multi-layer build up, crack resistant deposits. Fe-Cr-Ni-Mo-V alloy resists deformation due to impact & compressive loads | -- | - 40 – 46 HRc (as welded) - 28 – 45 HRc (after tempering at 550-6000C for 1 hr per inch job thickness) |
| EWAC G-572 P | Multi-layer build up, crack resistant deposits. Deposit resists deformation due to pressure & impact. High deposition rate & machinable deposit with carbide tip tool | -- | - 50 – 56 HRc (as welded) - 48 – 45 HRc (after tempering at 550-6000C for 1 hr per inch job thickness) |
More Products
EWAC Cold Repair Compound System
Ideal for emergency repairs. Typical application-Oil....
EWAC Thermal Spray Powder Delivery System
Boron Carbide Deposits-Retains high....